B87MnQL盘条电阻对焊焊接接头的组织与性能

Microstructure and mechanical properties of RBW joint with B87MnQL steel wire rod

Microstructure and mechanical properties of RBW joint with B87MnQL steel wire rod

doi:
10.7512/j.issn.1001-2303.2017.12.20
摘要:
为了提高B87MnQL盘条电阻对焊焊接(RBW)性能,以B87MnQL盘条为研究材料,运用优化的焊接参数进行电阻对焊,对焊接接头进行室温拉伸试验及多道次拉拔、热镀锌以及稳定化处理.借助光学显微镜和扫描电镜,分析不同的焊后热处理工艺时焊接接头组织的变化情况,探讨B87MnQL盘条焊接区域的断口形貌,研究B87MnQL盘条通过拉拔、热镀锌和稳定化处理的力学性能.结果显示,B87MnQL镀锌钢丝产品的性能完全符合国家标准的要求.
Abstract:
In order to improve the properties of RBW joints with B87MnQL wire rod steel,using the B87MnQL steel wire rod as the test material to carry out the RBW test by optimized parameters.And the tensile test at room temperature,multi-pass drawing,hot dip galvanizing and stabilizing treatment are carried out on welded joints.By OM and SEM,the change of microstructure of welded joints with different postweld heat treatments is analyzed,the appearance of fracture of welding area of B87MnQL steel wire rod is discussed,and the mechanical properties of B87MnQL after drawing,hot dip galvanizing and stabilizing treatment are studied.The result shows that the properties of B87MnQL galvanized steel wire completely meet the requirements of national standards.
作者 李养良 李海洲 张楚 张德勤 都学飞 潘东
Author: LI Yangliang LI Haizhou ZHANG Chu ZHANG Deqin DU Xuefei PAN Dong
作者单位 九江学院,江西九江,332005
期 刊: 电焊机 ISTIC EI SCI PKU CSSCI
Journal: Electric Welding Machine
年,卷(期) 2017, 47(12)
分类号 TG156
关键词: B87MnQL盘条 知识脉络 电阻对焊(RBW) 知识脉络 焊后热处理 知识脉络 力学性能 知识脉络 国家标准 知识脉络
Keywords: B87MnQL steel wire rod resistance butt welding (RBW) postweld heat treatment mechanical properties national standard
机标分类号 TG4 TG1
基金项目 九江学院校级科研项目,江西省教育厅科技落地计划项目,江西省科技计划项目,江西省“卓越工程师教育培养计划”实施成果
参考文献和引证文献
返回顶部参考文献
返回顶部引证文献
返回顶部本文读者也读过
返回顶部相似文献
返回顶部相关博文

知识产权声明| 服务承诺| 联系我们| 人才招聘| 客户服务| 关于我们

京ICP证:010071  互联网出版许可证:新出网证(京)字042号  京公网安备11010802020237号
万方数据知识服务平台--国家科技支撑计划资助项目(编号:2006BAH03B01)©北京万方数据股份有限公司  万方数据电子出版社